Input interpretation
![elements | magnetic properties](../image_source/0dfd095dcb6ed87f20107bfa71713cb4.png)
elements | magnetic properties
Results
![Curie point | median | 222 K | highest | 1394 K (cobalt) | lowest | 20 K (holmium) | distribution | Néel point | median | 100 K | highest | 393 K (chromium) | lowest | 12.5 K (cerium) | distribution | volume magnetic susceptibility | median | 1.29×10^-5 | highest | 0.1117784 (terbium) | lowest | -1.7×10^-4 (bismuth) | distribution | mass magnetic susceptibility | median | 4.94×10^-9 m^3/kg | highest | 1.36×10^-5 m^3/kg (terbium) | lowest | -2.48×10^-8 m^3/kg (hydrogen) | distribution | molar magnetic susceptibility | median | 2.42×10^-10 m^3/mol | highest | 2.161385×10^-6 m^3/mol (terbium) | lowest | -3.6×10^-9 m^3/mol (bismuth) | distribution |](../image_source/ca49c69888e37b14b50f0d076dfe2262.png)
Curie point | median | 222 K | highest | 1394 K (cobalt) | lowest | 20 K (holmium) | distribution | Néel point | median | 100 K | highest | 393 K (chromium) | lowest | 12.5 K (cerium) | distribution | volume magnetic susceptibility | median | 1.29×10^-5 | highest | 0.1117784 (terbium) | lowest | -1.7×10^-4 (bismuth) | distribution | mass magnetic susceptibility | median | 4.94×10^-9 m^3/kg | highest | 1.36×10^-5 m^3/kg (terbium) | lowest | -2.48×10^-8 m^3/kg (hydrogen) | distribution | molar magnetic susceptibility | median | 2.42×10^-10 m^3/mol | highest | 2.161385×10^-6 m^3/mol (terbium) | lowest | -3.6×10^-9 m^3/mol (bismuth) | distribution |
Units