Input interpretation
elements | Brinell hardness
Summary
0.14 MPa | 0.216 MPa | 0.363 MPa | 0.69 MPa | 8.83 MPa | 24.5 MPa | 26.4 MPa | 37.3 MPa | 38.3 MPa | 51 MPa | 60 MPa | 94.2 MPa | 167 MPa | 180 MPa | 196 MPa | 203 MPa | 245 MPa | 260 MPa | 265 MPa | 294 MPa | 343 MPa | 363 MPa | 392 MPa | 400 MPa | 412 MPa | 441 MPa | 471 MPa | 481 MPa | 490 MPa | 500 MPa | 589 MPa | 600 MPa | 628 MPa | 650 MPa | 677 MPa | 700 MPa | 716 MPa | 736 MPa | 746 MPa | 750 MPa | 800 MPa | 814 MPa | 874 MPa | 893 MPa | 1100 MPa | 1120 MPa | 1320 MPa | 1440 MPa | 1500 MPa | 1670 MPa | 1700 MPa | 2160 MPa | 2400 MPa | 2450 MPa | 2570 MPa | 3920 MPa | 7270 MPa (based on 60 values; 58 unavailable)
Entities with missing values
hydrogen | helium | lithium | boron | carbon | nitrogen | oxygen | fluorine | neon | silicon | ... (total: 58)
Distribution plots
(Brinell hardness in megapascals)
Brinell hardness rankings
1 | cesium | 0.14 MPa 2 | rubidium | 0.216 MPa 3 | potassium | 0.363 MPa 4 | sodium | 0.69 MPa 5 | indium | 8.83 MPa 6 | silver | 24.5 MPa 7 | thallium | 26.4 MPa 8 | palladium | 37.3 MPa 9 | lead | 38.3 MPa 10 | tin | 51 MPa ⋮ | | 51 | arsenic | 1440 MPa 52 | molybdenum | 1500 MPa 53 | iridium | 1670 MPa 54 | hafnium | 1700 MPa 55 | ruthenium | 2160 MPa 56 | uranium | 2400 MPa 57 | gold | 2450 MPa 58 | tungsten | 2570 MPa 59 | osmium | 3920 MPa 60 | germanium | 7270 MPa (based on 60 values; 58 unavailable)